Varilla de acero inoxidable
Especificación
| Tamaño de hilo | M2 | M2.5 | M3 | (M3.5) | M4 | M5 | M6 | M8 | M10 | M12 | (M14) | M16 | (M18) |
| d |
|
|
|
|
|
|
|
|
|
|
|
|
|
| P | Dientes gruesos | 0.4 | 0.45 | 0.5 | 0.6 | 0.7 | 0.8 | 1 | 1.25 | 1.5 | 1.75 | 2 | 2 | 2.5 |
| Dentículo | / | / | / | / | / | / | / | 1 | 1.25 | 1.25 | 1.5 | 1.5 | 1.5 |
| Dentículo | / | / | / | / | / | / | / | / | 1 | 1.5 | / | / | / |
| L | ± 10 | 1000 | 1000 | 1000 | 1000 | 1000 | 1000 | 1000 | 1000 | 1000 | 1000 | 1000 | 1000 | 1000 |
| Mil piezas de peso (acero) ≈kg | 18.7 | 30 | 44 | 60 | 78 | 124 | 177 | 319 | 500 | 725 | 970 | 1330 | 1650 |
| Tamaño de hilo | M20 | (M22) | M24 | (M27) | M30 | (M33) | M36 | (M39) | M42 | (M45) | M48 | (M52) |
| d |
|
|
|
|
|
|
|
|
|
|
|
|
| P | Dientes gruesos | 2.5 | 2.5 | 3 | 3 | 3.5 | 3.5 | 4 | 4 | 4.5 | 4.5 | 5 | 5 |
| Dentículo | 1.5 | 1.5 | 2 | 2 | 2 | 2 | 3 | 3 | 3 | 3 | 3 | 3 |
| Dentículo | / | / | / | / | / | / | / | / | / | / | / | / |
| L | ± 10 | 1000 | 1000 | 1000 | 1000 | 1000 | 1000 | 1000 | 1000 | 1000 | 1000 | 1000 | 1000 |
| Mil piezas de peso (acero) ≈kg | 2080 | 2540 | 3000 | 3850 | 4750 | 5900 | 6900 | 8200 | 9400 | 11000 | 12400 | 14700 |
Material
| SS316 Composición química (%) |
| Calificación | C≤ | Mn≤ | P≤ | S≤ | Si≤ | NI | Cr | Mes |
| 0.08 | 2.00 | 0.045 | 0.030 | 1 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 |
| 316 Propiedad mecánica |
| σb≥ | σ0.2≥ | Δ5 (%) ≥ | Dureza (HB) (KGF/MM2)] |
| 520 (MPA) | 205 (MPA) | 40% | ≤187 hrb≤90 hv ≤200 |
| 304 composición química (%) |
| Calificación | C≤ | Mn≤ | Si≤ | S≤ | P≤ | Cr | NI | N≤ |
| 0.08 | 2 | 0.75 | 0.03 | 0.045 | 18.0-20.0 | 8.0-10.5 | 0.1 |
| 304 Propiedad mecánica |
| σb≥ | σ0.2≥ | Δ5 (%) ≥ | Dureza (HB) (KGF/MM2)] |
| 520 (MPA) | 205 (MPA) | 40% | ≤187 hrb≤90 hv ≤200 |